Inshine EP803
Product Features
A UV-light-converting EPE encapsulant film, designed for PV modules requiring UV conversion, such as HJT cells. It has excellent UV-cutoff function within the 290-380nm range to ensure components durability, while converting harmful UV light into usable wavelengths to improve the photoelectric efficiency of the component.
Product characteristics
| TEST ITEMS | UNIT | REFERENCED STANDARDS | SPECIFICATION VALUE | |
| Width | mm | GB/T 13542.2-2009 | standard value（0-+8） | |
| Grammage | g/m2 | ISO 536-2012 | ≥standard value | |
| Tensile strength（MD） | MPa | GB/T 13542.2-2009 | ≥10 | |
| Tensile strength（TD） | MPa | GB/T 13542.2-2009 | ≥10 | |
| Elongation at break（MD） | % | GB/T 13542.2-2009 | ≥550 | |
| Elongation at break（TD） | % | GB/T 13542.2-2009 | ≥550 | |
| Heat shrinkage rate（120℃×3min）MD | % | GB/T 13542.2-2009 | ≤3.0 | |
| Heat shrinkage rate（120℃×3min）TD | % | GB/T 13542.2-2009 | ≤1.5 | |
|
Peel strength with Glass |
N/cm | GB/T 2790-1995 |
≥70 |
|
|
Transmittance（380-1100nm） |
% |
T/CPIA 0006-2017 |
≥90 |
|
|
Transmittance（290-38nm） |
% | T/CPIA 0006-2017 |
≥30 |
|
|
Volume resistivity |
Ω·cm |
GB/T 1410-2006 |
≥1×1015 |
|
|
Breakdown strength (AC method) |
KV/mm |
GB/T 1408.1-2016 |
≥30 |
|
|
Comparative tracking Index (CTI) |
V |
GB/T 4207-2012 |
≥400 |
|
|
Crosslinking degree (xylene method) |
% |
GB/T 29848-2013 |
75-95 | |
|
Water vapor transmission rate(38℃x90%RH) |
g/(m2·day) |
GB/T 26253-2010 |
≤15 | |
|
Anti migration performance (105℃, 96h ) |
cm |
-- |
≤0.2 |
|
| Constant damp heat test 85℃×85%RH 1000H | Yellowing index△YI | -- | IEC 61215-2 2016 | ≤3.0 |
| Peel strength with glass | N/cm | ≥40 | ||
| UV aging resistance test 120KWh/m2 | Yellowing index△YI | -- | IEC 61215-2 2016 | ≤3.0 |
| Peel strength with glass | N/cm | ≥40 | ||
| PCT High temperatureand high humidityexperiment48H | Yellowing index△YI | -- | T/CPIA0004-2017 | ≤3.0 |
| Peel strength with glass | N/cm | ≥40 | ||